High-temperature operating life

High-temperature operating life (HTOL) is a reliability test applied to integrated circuits (ICs) to determine their intrinsic reliability. This test stresses the IC at an elevated temperature, high voltage and dynamic operation for a predefined period of time. The IC is usually monitored under stress and tested at intermediate intervals. This reliability stress test is sometimes referred to as a "lifetime test", "device life test" or "extended burn in test" and is used to trigger potential failure modes and assess IC lifetime.

There are several types of HTOL:

HTOL Types Schematic Description
Static
IC stressed at static and constant conditions, IC not toggling.
Dynamic
Input stimulus for toggling the internal nodes of the device.
Monitored
Input stimulus for toggling the internal nodes of the device. Live output indicates IC performance.
In-situ tested
Input stimulus for toggling the internal nodes of the device. Responsive output tests IC performance.

Design considerations

The main aim of the HTOL is to age the device such that a short experiment will allow the lifetime of the IC to be predicted (e.g. 1,000 HTOL hours shall predict a minimum of "X" years of operation). Good HTOL process shall avoid relaxed HTOL operation and also prevents overstressing the IC. This method ages all IC's building blocks to allow relevant failure modes to be triggered and implemented in a short reliability experiment. A precise multiplier, known as the Acceleration Factor (AF) simulates long lifetime operation.

The AF represents the accelerated aging factor relative to the useful life application conditions.

For effective HTOL stress testing, several variables should be considered:

  1. Digital toggling factor
  2. Analog modules operation
  3. I/O ring activity
  4. Monitor design
  5. Ambient temperature (Ta)
  6. Junction temperature (Tj)
  7. Voltage stress (Vstrs)
  8. Acceleration factor (AF)
  9. Test duration (t)
  10. Sample size (SS)

A detailed description of the above variables, using a hypothetical, simplified IC with several RAMs, digital logic, an analog voltage regulator module and I/O ring, together with the HTOL design considerations for each are provided below.

Digital toggling factor

The digital toggling factor (DTF) represents the number of transistors that change their state during the stress test, relative to the total number of gates in the digital portion of the IC. In effect, the DTF is the percentage of transistors toggling in one time unit. The time unit is relative to the toggling frequency, and is usually limited by the HTOL setup to be in the range of 10–20Mhz.

Reliability engineers strive to toggle as many as possible transistors for each time unit of measure. The RAMs (and other memory types) are usually activated using the BIST function, while the logic is usually activated with the SCAN function, LFSR or logic BIST.

The power and the self-heating of the digital portion of the IC are evaluated and the device's aging estimated. These two measures are aligned so that they are similar to the aging of other elements of the IC. The degrees of freedom for aligning these measures are the voltage stress and/or the time period during which the HTOL program loops these blocks relative to other IC blocks.

Analog modules operation

The recent trend of integrating as many electronic components as possible into a single chip is known as system on a chip (SoC).

This trend complicates reliability engineers' work because (usually) the analog portion of the chip dissipates higher power relative to the other IC elements.

This higher power may generate hot spots and areas of accelerated aging. Reliability engineers must understand the power distribution on the chip and align the aging so that it is similar for all elements of an IC.

In our hypothetical SoC the analog module only includes a voltage regulator. In reality, there may be additional analog modules e.g. PMIC, oscillators, or charge pumps. To perform efficient stress tests on the analog elements, reliability engineers must identify the worst-case scenario for the relevant analog blocks in the IC. For example, the worst-case scenario for voltage regulators may be the maximum regulation voltage and maximum load current; for charge pumps it may be the minimum supply voltage and maximum load current.

Good engineering practice calls for the use of external loads (external R,L,C) to force the necessary currents. This practice avoids loading differences due to the chip's different operational schemes and operation trimming of its analog parts.

Statistical methods are used to check statistical tolerances, variation and temperature stability of the loads used, and to define the right confidence bands for the loads to avoid over/under stress at HTOL operating range. The degrees of freedom for aligning the aging magnitude of analog parts is usually the duty-cycle, external load values and voltage stress.

I/O ring activity

The interface between the "outside world" and the IC is made via the input/output (I/O) ring. This ring contains power I/O ports, digital I/O ports and analog I/O ports. The I/Os are (usually) wired via the IC package to the "outside world" and each I/O executes its own specific command instructions, e.g. JTAG ports, IC power supply ports etc. Reliability engineering aims to age all I/Os in the same way as the other IC elements. This can be achieved by using a Boundary scan operation.

Monitor design

As previously mentioned, the main aim of the HTOL is aging the samples by dynamic stress at elevated voltage and/or temperature. During the HTOL operation, we need to assure that the IC is active, toggling and constantly functioning.

At the same time, we need to know at what point the IC stops responding, these data are important for calculating price reliability indices and for facilitating the FA. This is done by monitoring the device via one or more vital IC parameters signals communicated and logged by the HTOL machine and providing continuous indication about the IC's functionality throughout the HTOL run time. Examples of commonly used monitors include the BIST "done" flag signal, the SCAN output chain or the analog module output.

There are three types of monitoring:

  1. Pattern matching: The actual output signal is compared to the expected one and alerts about any deviation. The main disadvantage of this monitor type is its sensitivity to any minor deviation from the expected signal. During the HTOL, the IC runs at a temperature and/or voltages that occasionally fall outside its specification, which may cause artificial sensitivity and/or a malfunction that fails the matching but is not a real failure.
  2. Activity: Counts the number of toggles and if the results are higher than a predefined threshold the monitor indicates OK. The main disadvantage of this type of monitoring is the chance that unexpected noise or signal could be wrongly interpreted. This issue arises mainly in the case of low count toggling monitor.
  3. Activity within a predefine range: Checks that the monitor responds within a predefined limit, for example when then number of toggles is within a predefined limit or the output of the voltage regulator is within a predefined range.

Ambient temperature (Ta)

According to JEDEC standards, the environmental chamber should be capable of maintaining the specified temperature within a tolerance of ±5 °C throughout while parts are loaded and unpowered. Today's environmental chambers have better capabilities and can exhibit temperature stability within a range of ±3 °C throughout.

Junction temperature (Tj)

Low power ICs can be stressed without major attention to self-heating affects. However, due to technology scaling and manufacturing variations, power dissipation within a single production lot of devices can vary by as much as 40%. This variation, in addition to high power IC makes advanced contact temperature controls necessary for facilitating individual control systems for each IC

Voltage stress (Vstrs)

The operating voltage should be at least the maximum specified for the device. In some cases a higher voltage is applied to obtain lifetime acceleration from voltage as well as temperature.

To define the maximum permitted voltage stress, the following methods can be considered:

  1. Force 80% of breakdown voltage;
  2. Force six-sigma less than the breakdown voltage;
  3. Set the overvoltage to be higher than the maximum specified voltage. An overvoltage level of 140% of the maximum voltage is occasionally used for MIL and automotive applications.

Reliability engineers must check that Vstress does not exceed the maximum rated voltage for the relevant technology, as specified by the FAB.

Acceleration factor (AF)

The Acceleration factor (AF) is a multiplier that relates a product’s life at an accelerated stress level to the life at the use stress level.

An AF of 20 means 1 hour at stress condition is equivalent to 20 hours at useful condition.

The voltage acceleration factor is represented by AFv. Usually the stress voltage is equal to or higher than the maximum voltage. An elevated voltage provides additional acceleration and can be used to increase effective device hours or achieve an equivalent life point.

There are several AFv models:

  1. E model or the constant field/voltage acceleration exponential model;
  2. 1/E model or, equivalently, the anode hole injection model;
  3. V model, where the failure rate is exponential to voltage
  4. Anode hydrogen release for the power-law model

AFtemp is the acceleration factor due to changes in temperature and is usually based on the Arrhenius equation. The total acceleration factor is the product of AFv and AFtemp

Test duration (t)

The reliability test duration assures the device’s adequate lifetime requirement.

For example, with an activation energy of 0.7 eV, 125 °C stress temperature and 55 °C use temperature, the acceleration factor (Arrhenius equation) is 78.6. This means that 1,000 hours' stress duration is equivalent to 9 years of use. The reliability engineer decides on the qualification test duration. Industry good practice calls for 1,000 hours at a junction temperature of 125 °C.

Sample size (SS)

The challenge for new reliability assessment and qualification systems is determining the relevant failure mechanisms to optimize sample size.

Sample plans are statistically derived from manufacturer risk, consumer risk, and the expected failure rate. The commonly used sampling plan of zero rejects out of 230 samples is equal to three rejects out of 668 samples assuming LTPD =1 and a 90% confidence interval.

HTOL policy

Sample selection

Samples shall include representative samples from at least three nonconsecutive lots to represent manufacturing variability. All test samples shall be fabricated, handled, screened and assembled in the same way as during the production phase.

Sample preparation

Samples shall be tested prior to stress and at predefined checkpoints. It is good engineering practice to test samples at maximum and minimum rating temperatures as well as at room temperature. Data logs of all functional and parametric tests shall be collated for further analysis.

Test duration

Assuming Tj = 125 °C, commonly used checkpoints are after 48, 168, 500 and 1,000 hours.

Different checkpoints for different temperatures can be calculated by using the Arrhenius equation. For example, with an activation energy of 0.7e V, Tj of 135°C and Tuse of 55 °C the equivalent checkpoints will be at 29, 102, 303 and 606 hours.

Electrical testing should be completed as soon as possible after the samples are removed. If the samples cannot be tested soon after their removal, additional stress time should be applied. The JEDEC standard requires samples be tested within 168 hours of removal.

If testing exceeds the recommended time window, additional stress should be applied according to the table below:[2]

Time above recommended time window 0h < h ≤ 168h 168h < h ≤ 336h 336h < h ≤ 504h Other
Additional stress hours 24h 48h 72h 24 hours for each 168 hours

Merit numbers

The merit number is the outcome of statistical sampling plans.

Sampling plans are inputted to SENTENCE, an audit tool, to ensure that the output of a process meets the requirements. SENTENCE simply accepts or rejects the tested lots. The reliability engineer implements statistical sampling plans based on predefined Acceptance Quality Limits, LTPD, manufacturer risk and customer risk. For example, the commonly used sampling plan of 0 rejects out of 230 samples is equal to 3 rejects out of 668 samples assuming LTPD=1.

HTOL in various industries

The aging process of an IC is relative to its standard use conditions. The tables below provide reference to various commonly used products and the conditions under which they are used.

Reliability engineers are tasked with verifying the adequate stress duration. For example, for an activation energy of 0.7eV, a stress temperature of 125 °C and a use temperature of 55 °C, an expected operational life of five years is represented by a 557-hour HTOL experiment.

Commercial use

Min tuse Max tuse Description expected life time
5 °C 50 °C desktop products 5 years
0 °C 70 °C mobile products 4 years

Automotive use

Example Automotive Use Conditions[1]

Min Tuse Max tuse Description Expected life time
−40 °C 105—150 °C under hood condition 10 to 15 years
−40 °C 80 °C passenger compartment condition 10 to 15 years
0 °C 70 °C passenger compartment condition 10 to 15 years

Telecommunication use

Example European Telecom use Conditions definition

Min Tuse Max Tuse Description expected life time
5 °C 40 °C class 3.1 Temperature-controlled locations usually 25 years
−5 °C 45 °C class 3.2 Partly temperature-controlled locations usually 25 years
−25 °C 55 °C class 3.3 Not temperature-controlled locations usually 25 years
−40 °C 70 °C class 3.4 Sites with heat-trap usually 25 years
−40 °C 40 °C class 3.5 Sheltered locations, Direct solar radiation usually 25 years

Example US Telecom use conditions definition

Min Tuse Max Tuse Description expected life time
−40 °C 46 °C Uncontrolled environment 25 years
5 °C 40 °C Enclosed building 25 years

Military use

Example military use conditions

Min Tuse Max Tuse Description
−55 °C 125 °C MIL products
−55 °C up to 225 °C high-temp applications

See also

References

This article is issued from Wikipedia - version of the 4/13/2015. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.